ObjectiveThis study examined the effect of the manufacturing methods (ground, electropolished, and twisted) and the cross-sectional area (CSA) of nickel-titanium (NiTi) rotary instruments on their cyclic fatigue resistance.Study designA total of 80 NiTi rotary instruments (ISO 25/.06 taper) from 4 brands (K3, ProFile, RaCe, and TF) were rotated in a simulated root canal with pecking motion until fracture. The number of cycles to failure (NCF) was calculated. The CSA at 3 mm from the tip of new instruments of each brand was calculated. The correlation between the CSA and NCF was evaluated. All fractured surfaces were analyzed using a scanning electron microscope to determine the fracture mode.ResultsThe TF instruments were the most resistant to fatigue failure. The resistance to cyclic failure increased with decreasing CSA. All fractured surfaces showed the coexistence of ductile and brittle properties.ConclusionThe CSA had a significant effect on the fatigue resistance of NiTi rotary instruments.