Effect of stress corrosion cracking at various strain rates on the electrochemical corrosion behavior of Mg-Zn-In-Sn alloy

This study is aimed to determine the effect of stress corrosion with low strain rates on the electrochemical properties of alloy electrode. Stress corrosion cracking tests of Mg-Zn-In-Sn alloy in 3.5 wt.% sodium chloride solutions at 25°C were performed. The effects of the electrochemical properties under the stress corrosion with low strain rates were investigated. The microstructures of cross section were observed by optical microscope. The results showed that the ultimate tensile strengths of Mg-Zn-In-Sn alloy increased and the strain decreased as the strain rates increased. Open circuit potentials (OCP) of Mg-Zn-In-Sn alloy electrode possess stability and the loop currents (LC) were improved with the increasing of stress in the elastic zone. The variation of OCP and LC did not change with the increasing of strain-rate. The microstructure of cross section observing revealed the mechanism of OCP and LC changing