The aqueous-phase hydrodeoxygenation (APHDO) of 1-propanol at 230 °C and 35 bar was studied over 1 wt.% Pt catalysts supported on several metal oxides. Pt catalysts supported on amorphous silica, alumina and niobia aerogels, and crystalline niobic acid calcined at 500 °C showed low activities or deactivation. Under the APHDO condition, these supports experienced a structure transformation to crystalline quartz, boehmite and niobia TT phase. Pt/Nb2O5–Al2O3 aerogel also suffered from the same crystallization behavior. In contrast, Pt/Nb2O5–SiO2 aerogels with different Nb/(Nb + Si) ratios maintained a good catalytic performance for prolonged reaction periods. Through characterizations of spent catalysts, Nb2O5–SiO2 aerogels were found to retain X-ray amorphous and porous structure. Also, their acid site densities were negligibly changed during the reaction. The catalysts with the Nb / (Nb + Si) ratio of 0.500 and 0.575 reached the molar propane/ethane ratio of about 1.0, indicating that Pt/Nb2O5–SiO2 aerogel catalysts are highly active in the presence of water.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Pt/Nb2O5–SiO2 aerogels showed a superior catalytic activity for prolonged periods. ► The hydrothermal reaction condition led to the crystallization of support materials. ► SiO2 and Al2O3 aerogels were transformed into quartz and boehmite, respectively. ► Nb2O5 and Nb2O5–Al2O3 aerogels suffered from the similar crystallization behavior. ► Original properties of Nb2O5–SiO2 aerogels were maintained during the reaction.