Abstract
Tribological behaviour of steel APS coating and TiO2 APS coating was investigated and compared with reference steel material under boundary lubrication in presence of MoDTC. Significant friction and wear reduction was observed in case of TiO2 APS coating compared to conventional steel and steel APS coating. This was due to the formation of pure MoS2 in the form of long crystalline flakes directly attached to TiO2 substrate. Friction was slightly higher in case of steel since Mo-oxysulphide formation was observed along with some MoS2 flakes embedded in an amorphous matrix. Effect of roughness and addition of ZDDP on MoDTC decomposition mechanism was discussed. Tribocatalytic effect was proposed to explain the complete decomposition of MoDTC in steel/TiO2 APS contact.
Keywords
Related Topics
Physical Sciences and Engineering
Chemical Engineering
Colloid and Surface Chemistry
Authors
P. Deshpande, C. Minfray, F. Dassenoy, B. Thiebaut, Th. Le Mogne, B. Vacher, F. Jarnias,