Dewatering of 2,2,3,3-tetrafluoropropan-1-ol by hydrophilic pervaporation with poly(vinyl alcohol) based Pervap™ membranes

It was found that all membranes were hydrophilic (CA < 90°) and the polar component of SFE was much higher than the dispersive one. The apparent activation energy for water transport was very high (Eapp = 81.3 kJ/mol), indicated that water transport is activated thermally. Pervap™ membranes were very selective during the dehydration process of TFP. In contact with the Pervap™ 2200, 2201, and 2216 permeate contained practically pure water, regardless the feed composition. The process separation index (PSI) for Pervap™ 2200 and 2216 was close to 5000 kg m−2 h−1, suggesting that both membranes can be efficiently applied in the batch pervaporation process for TFP dehydration.