| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 4999185 | Progress in Organic Coatings | 2017 | 10 Pages |
Abstract
The results showed a correlation between protective properties and viscoelastic behavior of coatings. It was found that a sample with higher percentage of cycloaliphatic hardener has higher elastic modulus (1275 MPa) and a sample with higher percentage of polyether poly amine hardener has the lower elastic modulus (465 MPa). Additionally It was found that a sample with excellent initial protective properties (|Z| = 1010 Ω cm2), higher elastic modulus and low initial water permeability (0.308 g/m2hr) may quickly fail because of the adhesion failure after wet cycles.