Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
5021976 | Composites Science and Technology | 2017 | 23 Pages |
Abstract
An electric field is used to align carbon nanofibres (CNFs) in the matrix of a glass-fibre reinforced-polymer (GFRP) composite to simultaneously improve the (a) delamination toughness, (b) electrical conductivity, and (c) damage-sensing capability. The CNFs are added to the epoxy resin prior to the manufacture of the GFRP composites. To align the CNFs, an alternating current (AC) electric field of 30Â V/mm at 10Â kHz is applied across the GFRP sheet throughout the matrix-curing process. The electromechanical force induced by the electric field, applied in the through-thickness direction of the composite sheet, rotates and aligns the CNFs in the direction of the applied electric field prior to the gelation of the epoxy matrix. After curing, the resultant aligned, 'chain-like', microstructure of the CNFs in the epoxy matrix significantly enhances both the interlaminar fracture toughness and the through-thickness electrical conductivity of the GFRP composite. Specifically, the addition of 0.7Â vol% of randomly-orientated CNFs in the GFRP composite yielded an â¼50% and 25% increase in the values of the mode I fracture toughness pertinent to the initiation, GIci, and steady-state growth, GIcss, of delamination crack, respectively, compared to the control GFRP composite. The alignment of the CNFs, in the transverse direction to the direction of the crack growth, increases the mode I toughness values of GIci and GIcss by â¼100% and â¼80%, respectively, compared to the control GFRP composite. These significant increases are attributable to multiple toughening mechanisms, including debonding of the CNFs from the matrix, void growth of the epoxy matrix, pull-out and rupture of the CNFs. Further, the electric-field induced alignment of the CNFs, in the through-thickness direction, increases the out-of-plane electrical conductivity of the GFRP by about twenty-six times, compared to the GFRP composite containing randomly-orientated CNFs. Of particular interest, the damage-sensing capacity is enhanced for the GFRP composite with aligned CNFs in the epoxy matrix, which stems from the greatly increased out-of-plane electrical conductivity, as confirmed by a modelling study. Therefore, this present work has identified a new strategy to develop GFRP composites with greatly improved delamination toughness, electrical conductivity, and higher crack-detection sensitivity.
Related Topics
Physical Sciences and Engineering
Engineering
Engineering (General)
Authors
Shuying Wu, Raj B. Ladani, Anil R. Ravindran, Jin Zhang, Adrian P. Mouritz, Anthony J. Kinloch, Chun H. Wang,