Abstract
The different effect of corrosive environment on fatigue crack initiation is demonstrated in the plate bending fatigue testing results of 1% carbon steel and13Cr-1Mo steel in refrigeration compressor gaseous environment. For 1% carbon steel fatigue crack initiated from subsurface at lower fatigue life of 5x106 cycles,while fatigue crack initiated from surface corrosion pit at higher fatigue life of 5x106 cycles. For 13Cr-1Mo steel subsurface fatigue crack initiation was predominantly observed in air and in refrigeration compressor gaseous environment.