Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
5184764 | Polymer | 2011 | 8 Pages |
It is shown that the incorporation of interleaved films has major advantages for the production of polyethylene single polymer composites by the process of selective melting (termed hot compaction). The key issue is to choose a compaction temperature which melts the minimum amount of the original oriented elements whilst achieving acceptable bonding within the compacted structure. Utilising an interleaved film, excellent interlayer peel strengths can be achieved at lower compaction temperatures giving greater retention of the oriented fraction of the original fibres or tapes and a wider processing window. For example, using a very high modulus, ultra-high molecular weight, polyethylene tape, together with an interleaved film, resulted in an in-plane modulus of 25Â GPa, an in-plane strength of 500Â MPa, and an interlayer strength of >10Â N/10Â mm. These are amongst the highest values reported for a single polymer composite. Other important factors have been investigated including fabric weave style and whether it is better to use fibres or tapes as the oriented reinforcement.
Graphical abstractDownload full-size image