Gas foaming of segmented poly(ester amide) films

Two poly(ester amide)s with 25 mol% (PEA2,5-25) and 50 mol% (PEA2,5-50) of bisamide segment content were foamed at 70 and 105 °C, respectively. The storage modulus (G′) of both pure polymers at the onset foaming temperature is 50-60 MPa. Closed-cell foams were obtained with a maximum porosity of ∼90%. The average pore size of PEA2,5-25 ranges from 77 to 99 μm. In contrast, the average pore size of PEA2,5-50 is in between 2 and 4 μm and can be increased to 100 μm by lowering the CO2 saturation pressure to 20 bar. The porosity of PEA2,5-50 foams using this saturation pressure decreased to 70%.