Chemical modification of copolyimides with bulky pendent groups: Effect of modification on solubility and thermal stability

Two novel copolyimides bearing bulky pendent groups have been prepared by chemical modification of a copolyimide precursor containing carboxylic acid groups. The incorporation of the bulky groups was achieved by esterification of the copolyimide containing carboxylic acid groups with 4-tert-butylbenzyl alcohol. By controlling the carboxylic acid/alcohol ratio, two different degrees of modification were obtained. The actual composition of the modified polymer was estimated by 1H NMR. They showed better solubility than the copolyimide precursor, where 100% modification yielded the copolyimide with the highest solubility properties. Thermal analyses indicated that the incorporation of bulky pendent groups has a moderate effect on decreasing the thermal degradation temperature and the glass transition temperature.