Material PropertiesLarge impact in electrical properties of polypropylene by improving the filler-matrix interface effect in PP/PS blends

Inorganic nanoparticles are widely used to improve space charge behavior, DC breakdown strength and other electrical properties of polymer insulating materials, but the uniform distribution of inorganic nanofillers in matrix is difficult due to their agglomeration and bad compatibility with the polymeric matrix. In this paper, polypropylene (PP)/polystyrene (PS) blends were prepared to suppress space charge accumulation and improve DC breakdown strength. Polypropylene-g-polystyrene (PP-g-PS) graft copolymer was used as compatibilizer to improve the compatibility of PP matrix and PS filler. The evolution of microstructure of PP/PS blends were investigated by scanning electron microscope (SEM), the space charge distributions were measured by a pulsed electro-acoustic (PEA) system, and DC breakdown strength was also tested. The morphologies show that the size of PS particles reduced to 310 nm when the content of PP-g-PS graft copolymer increased to 24 wt%, and the interaction between PP matrix and PS particles enhanced. The presence of PS particles in all PP/PS blends suppressed the space charge accumulation compared to neat PP, but the DC breakdown strength in uncompatibilized blend was lower than neat PP. The increasing of content of PP-g-PS improved the DC breakdown strength with the maximum value of 408.9 kV/mm was obtained. This may attribute to excellent interface structure formed between PP matrix and PS particles.