Fabrication and enhanced mechanical properties of porous PLA/PEG copolymer reinforced with bacterial cellulose nanofibers for soft tissue engineering applications

A new class of polylactic acid (PLA)/polyethylene glycol (PEG) copolymer reinforced with bacterial cellulose nanofibers (BC) was prepared using a solvent casting and particulate leaching methods. Four weight fractions of BC (1, 2.5, 5, and 10 wt%) were incorporated into copolymer via silane coupling agent. Mechanical properties were evaluated using response surface method (RSM) to optimize the impact of pore size, porosity, and BC contents. Compressive strength obtained for PLA/PEG-5 BC wt% was 9.8 MPa, which significantly dropped after developing a porous structure to 4.9 MPa. Nielson model was applied to investigate the BC stress concentration on the PLA/PEG. Likewise, krenche and Hapli-Tasi model were employed to investigate the BC nanofiber reinforcement and BC orientation into PLA/PEG chains. The optimal parameters of the experiment results found to be 5 wt% for BC, 230 μm for pore size, and 80% for porosity. Scanning electron microscopy (SEM) micrograph indicates that uniform pore size and regular pore shape were achieved after an addition of BC-5% into PLA/PEG. The weight loss of copolymer-BC with scaffolds enhanced to the double values, compared with PLA/PEG-BC % without scaffolds. Differential Scanning Calorimetric (DSC) results revealed that the BC nanofiber improved glass transition temperature (Tg) 57 °C, melting temperature (Tm) 171 °C, and crystallinity (χ %) 43% of PLA/PEG reinforced-BC-5%.

Graphical abstractDownload high-res image (221KB)Download full-size image