Nonisothermal crystallization behavior, and morphology of poly(trimethylene terephthalate)/polyethylene glycol copolymers

Poly(trimethylene terephthalate)/polyethylene glycol (PTT/PEG) copolymers, with PEG content ranging from 27.2 to 47.4 wt%, were synthesized by melt copolycondensation. Wide-Angle X-ray diffractometer revealed that all copolymers had the same crystal structure of homo-PTT at room temperature. All copolymers could form ring-banded spherulites, and band spacing increased with increasing PEG content at a given crystallization temperature. Nonisothermal crystallization morphology of copolymers was greatly influenced by cooling rate. When the cooling rate was 2.5 °C/min or lower, banded patterns were absent, whereas when the cooling rate was 20 °C/min or higher, a novel crystal morphology composed of non-banded spherulites (central part) and ring-banded spherulites with decreasing band spacing along the radial growth direction was observed. Moreover, the size of the non-banded spherulitic part decreased with increasing cooling rate. Finally, the nonisothermal crystallization kinetics of copolymers were analyzed and only the Mo method was satisfactory to accurately describe this system.