5348505 | Applied Surface Science | 2016 | 9 Pages |
Abstract
The tribo-chemical behavior of the eutectoid steel during rolling contact friction is investigated via scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy (XPS) and electron probe X-ray microanalysis. The worn surface is divided into three zones: matrix zone (without friction), tribo-film zone (formed during friction) and delamination zone (tribo-film spalling). The different chemical states of atoms between those three zones and the air were investigated using the XPS analysis. The results showed that the matrix zone is composed of Fe2O3, FeO and metallic Fe, while the tribo-film and delamination zones only contain Fe2O3 and FeO. Where the tribo-film is formed, the absorptive ability of O and C atoms on the top 2-3 atomic layers is probably weakened, while the exposed fresh metal in the delamination zone tends to be continuously oxidized and form tribo-film. The tribo-chemical reaction in the delamination zone is more activated than that in the other two zones. The protective nature of the tribo-film probably maintains a low friction coefficient under rolling contact friction condition.
Keywords
Related Topics
Physical Sciences and Engineering
Chemistry
Physical and Theoretical Chemistry
Authors
Y. Zhou, Z.B. Cai, J.F. Peng, B.B. Cao, X.S. Jin, M.H. Zhu,