Unique dielectric features of a ceramic-semiconductor nanocomposite MgNb2O6Â +Â 0.25Zn0.5Cd0.5S

The present communication deals with the optical/dielectric characteristics of MgNb2O6 + 0.25Zn0.5Cd0.5S nanocomposite (10-30 nm) mixture. Zn0.5Cd0.5S (size ∼10 nm) was synthesized by microwave assisted solvo-thermal method. Monophase magnesium niobate (MN) nanoparticles (10-20 nm) were synthesized in a single step by mechanochemical treatment of MgO + Nb2O5 under dry N2 atmosphere. The nanocomposite, MgNb2O6 + 0.25Zn0.5Cd0.5S, was prepared by mechanical admixing of MgNb2O6 and Zn0.5Cd0.5S taken in 4:1 molar ratio. The photoluminescence study shows violet, yellow and orange-red emissions by the MgNb2O6 + 0.25Zn0.5Cd0.5S composite. The observed dielectric constant value (ε) for MgNb2O6 + 0.25Zn0.5Cd0.5S is only 4.7, which is ∼5 times smaller than the ε value of MgNb2O6 while a dielectric loss for the composite being closer to zero ensures promising commercial applications.