Semiconducting nanocrystalline nickel oxide (NiO) and PdO-doped NiO heteromixture (2, 5 and 10 wt%) have been synthesized via a metal-citrate complex method. The obtained materials were further characterized using TG/DTA, FT-IR, UV-vis, XRD, XPS, BET/BJH, SEM and TEM analyses to determine their structural and morphological properties. The results indicated that the spherical, uniform PdO nanoparticles were densely deposited on the NiO surface mainly in diameters of 10-15 nm. Moreover, the existence of various defect states was also analyzed with the help of photoluminescence (PL) spectroscopy. The gas response characteristics of synthesized materials were evaluated in the presence and absence of toxic gases such as hydrogen sulfide (H2S), carbon monoxide (CO), liquid petroleum gas (LPG), and ethanol (C2H5OH). The experimental results revealed that the sensitivity and selectivity of the NiO-based sensor material are dependent on the weight% of PdO loading in the NiO nanopowder. Among the investigated compound, the 5 wt% PdO-doped NiO sensor material showed excellent sensitivity and selectivity to 100 ppm H2S with a fast response/recovery characteristics of 6 s and 10 s, respectively. Furthermore, the 5 wt% PdO-doped NiO based sensor showed a linear relationship between the different concentrations of H2S gas and a significantly higher response to H2S even at the low concentration of 20 ppm (43%) at 60 °C. The dominant H2S gas sensing mechanisms in the NiO and 5 wt% PdO-doped NiO nanomaterials are systematically discussed based on the obtained characterization results.
Keywords
Related Topics
Physical Sciences and Engineering
Chemistry
Physical and Theoretical Chemistry
Authors
C. Balamurugan, Y.J. Jeong, D.W. Lee,