One-pot electrodeposition of cobalt flower-decorated silver nanotrees for oxygen reduction reaction

•Bimetallic AgCo electrocatalyst was prepared by one-pot electrodeposition.•Ag nanotree backbones formed initially, followed by Co flower growth on them.•Deposition solution composition and deposition time were varied.•Various Ag to Co relative contents in AgCo catalysts were attained.•AgCo with 14% Co showed better or comparable performance to bare Pt for ORR.

In this paper, we demonstrate a simple fabrication of bimetallic silver (Ag) and cobalt (Co) nanostructures (AgCo) with various Ag to Co relative contents via electrochemical co-deposition. A series of AgCo catalysts was electrodeposited on glassy carbon (GC) electrodes at −0.57 V vs. SCE in the deposition solutions, containing Ag precursor, Co precursor, Triton X-100, and 0.3 M KNO3 aqueous solution, with various Ag to Co precursor concentration ratios (1:x, x was varied from 3 to 11). The films, deposited with the total deposition charge of 0.042C, were denoted as Ag1Cox. SEM and TEM analyses showed that Ag1Cox formed a structure consisted of flower-like Co grown on tree-like Ag backbones while it had more Co flowers with a greater x. The ORR activities were examined in 0.1 M NaOH solution with rotating disk electrode (RDE) voltammetry and Ag1Co7 showed the best catalytic activity. The co-deposition mechanism was further investigated by varying the deposition time of Ag1Co7. At the early stage of deposition, Ag-tree branches were formed predominantly, followed by the growth of flower-like Co nanostructures on the Ag nanotrees: More Co flowers were produced on Ag backbones with longer deposition time, being attributed to both a less negative reduction potential of Ag+ to Ag than Co2+ to Co and promoted Co2+ reduction on the initially formed Ag surface. Ag1Co7 electrodeposited for 200 s, consisted of ∼14% Co, showed the greatest ORR catalytic activity which was better or comparable to noble metal Pt.

Graphical abstractDownload high-res image (130KB)Download full-size image