Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
5357689 | Applied Surface Science | 2010 | 12 Pages |
Abstract
Hydrogen permeation measurements of 1.5-10 μm thick Pd/Ag23 wt% membranes before and after thermal treatments at 300 °C in air (both sides) or in the temperature range 300-450 °C in N2 (feed side) and Ar (permeate side) were performed. Accompanying changes in surface topography and chemical composition were subsequently investigated by atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) depth profiling. For a 2 μm thick membrane, the surface roughness increased for all annealing temperatures applied, while a temperature of 450 °C was required for an increase in roughness of both membrane surfaces to occur for the 5 μm membrane. The thickest membrane, of 10 μm, showed changed surface roughness on one side of the membrane only and a slight decrease in hydrogen permeance after all heat treatments in N2/Ar. X-ray photoelectron spectroscopy investigations performed after treatment and subsequent permeation measurements revealed segregation of silver to the membrane surfaces for all annealing temperatures applied. In comparison, heat treatment at 300 °C in air resulted in significantly increased hydrogen permeance accompanied by increasing surface roughness. Upon exposure to oxygen, Pd segregates to the surface to form a 2-3 nm thick oxide layer (PdO), with more complex segregation behavior after subsequent reduction and permeance measurements in pure hydrogen. The available permeance data for the Pd/Ag23 wt% membranes after heat treatment in air at 300 °C is found to depend linearly on the inverse membrane thickness, implying bulk limited hydrogen permeation for thicknesses down to 1.5-2.0 μm.
Related Topics
Physical Sciences and Engineering
Chemistry
Physical and Theoretical Chemistry
Authors
A. Ramachandran, W.M. Tucho, A.L. Mejdell, M. Stange, H.J. Venvik, J.C. Walmsley, R. Holmestad, R. Bredesen, A. Borg,