Synthesis of uniform and size-controllable carbon nanospheres by a simple hydrothermal method and fabrication of carbon nanosphere super-hydrophobic surface

A simple hydrothermal method was used to produce high yield, monodisperse and tightly controllable size of carbon nanospheres (CNSs) by adjusting the concentration of initial sucrose solution in a sealed autoclave at 170 °C for 8 h. By changing the solution concentration from 0.5 to 0.1 mol l−1, the sizes of carbon spheres (CS) were reduced from about 2500 to about 300 nm. Also by increasing the solution volume to the vessel volume ratio (Vs/Vv) from 5/6 to 11/13, the yield of CS was increased from 25% up to about 55% of initial raw materials. It was found that by post-annealing of the 300 nm CNSs at 435 °C for 30 min, their diameters were reduced to 100 nm. Moreover, annealing in air atmosphere had a noticeable influence on the surface functional groups and bonds of CNSs. In addition, CNSs were used to fabricate hydrophobic surfaces by coating their ethanolic colloidal solution on glass substrates. The measured contact angle (CA) of a water droplet was about 153°, indicating that the CNSs thick layers were super-hydrophobic. The size dependence of CNSs on the different parameters has been discussed.