Effect of ALD surface treatment on structural and optical properties of ZnO nanorods

In this study, we report on the improvement of the optical and structural properties of ZnO nanorods using atomic layer deposition (ALD) on seed ZnO nanorods. After the initial growth of ZnO seed nanorods by hydrothermal synthesis for 1 h, a ZnO layer with a thickness of 10 nm was deposited on the initial ZnO seed nanorods using ALD. Then ZnO was further grown by hydrothermal synthesis for 4 h. The samples were characterized using room temperature photoluminescence (PL), field emission-scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). From this experiment, it was found that the ZnO nanorods with the ALD surface treatment show improved optical and structural properties when compared with the ZnO nanorods grown only by hydrothermal synthesis. The ZnO nanorods with the ALD surface treatment show about 2.7 times higher XRD (0 0 2) peak intensity, about 2.64 times higher PL NBE peak intensity, and about 3.1 times better NBE/DLE ratio than the ZnO nanorods without an ALD surface treatment.