Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
5366179 | Applied Surface Science | 2006 | 4 Pages |
The purpose of this paper is to report some experimental results with HfSiO films formed on silicon substrates by electron beam evaporation (EB-PVD) and annealed at different temperatures. The images of atomic force microscope (AFM) indicated that HfSiO film annealed at 900 °C was still amorphous, with a surface roughness of 0.173 nm. X-ray photoelectron spectroscopy (XPS) analysis revealed that the chemical composition of the film was (HfO2)3(SiO2) and Hf-Si-O bonds existed in the annealed film. Electrical measurements showed that the equivalent oxide thickness (EOT) was 4 nm, the dielectric constant was around 6, the breakdown voltage was 10 MV/cm, the fixed charge density was â1.2 Ã 1012 cmâ2, and the leakage current was 0.4 μA/cm2 at the gate bias of 2 V for 6 nm HfSiO film. The annealing after deposition effectively reduced trapping density and the leakage current, and eliminated hysteresis in the C-V curves. Annealing also induced SiO2 growth at the interface.