Strain relaxation and surface morphology of high indium content InAlAs metamorphic buffers with reverse step

Low-temperature step-graded high indium content InAlAs (In% = 0.75) metamorphic buffer layers with reverse step layer grown on GaAs substrate by molecular beam epitaxy are investigated in this paper. The composition and the strain relaxation of the top InAlAs layer are determined by high-resolution triple-axis X-ray diffraction measurements, which show that the top InAlAs layer is nearly fully relaxed and the growth parameters for these samples have little influence on the strain relaxation ratio. Surface morphology is observed by reflection high-energy electron diffraction pattern and atomic force microscopy. The surface morphology is found to depend strongly on both the growth temperature and the As flux. Compared with other samples, the sample growth under the optimized conditions has the smallest value of root mean square surface roughness. Furthermore, the ω − 2θ and ω scans of the triple-axis X-ray diffraction and transmission electron microscopy result also show the sample grown under the optimized conditions has good crystalline quality.