Abstract
The survey scans corresponding to 400, 500 and 600 °C annealed ML sample shows interdiffusion and intermixing of Ni atoms into Ti layers leading to chemical Ti-Ni alloys phase formation at interface. The corresponding recorded VB spectra using synchrotron radiation at 134 eV on as-deposited ML sample with successive sputtering shows alternately photoemission bands due to Ti 3d and Ni 3d, respectively, indicating there is no mixing of the consequent layers and any phase formation at the interface during deposition. However, ML samples annealed at higher temperatures of annealing, particularly at 400, 500 and 600 °C show a clear shift in Ni 3d band and its satellite peak position to higher BE side indicates Ti-Ni alloy phase formation. In addition to this, reduction of satellite peak intensity and Ni 3d density of states (DOS) near Fermi level is also observed due to Ti-Ni phase formation with higher annealing temperatures. The variable photon energy VB measurements on as-deposited and ML samples annealed at 400 °C confirms existence and BE position of observed Ni 3d satellite structure. The observed changes and modifications in the VB photoemission are discussed and interpreted in terms of structural changes at the interface due to annealing treatment.
Related Topics
Physical Sciences and Engineering Chemistry Physical and Theoretical Chemistry
Authors
, ,