Abstract
The effect of nitrogen (N) incorporation into HfSiO on the electronic structure and band alignment of HfSiO films was investigated. N depth profile data obtained by medium energy ion scattering (MEIS) showed that the concentration of N or the bonding or electronic state of N in the film was stable when the film was annealed at 950 °C, while the oxygen (O) in HfSiON films was present in dissociated form, as evidenced by the unoccupied electronic state of O. The valence band offsets of the HfSiO films were strongly affected by N incorporation due to the presence of N in a 2p state. Moreover, a reduction in the conduction band offset of a HfSiO film was confirmed after the film was annealed in an atmosphere of N2. The unoccupied state of the O vacancy is responsible for the change in the conduction band offset. The results of ab-initio calculations for the density of states (DOS) of HfSiO and HfSiON supercells were in agreement with the experimental results. The incorporation on N into HfSiO prevents the formation of a gap-state inside the band gap despite the fact that an O vacancy is generated in the film.
Keywords
Related Topics
Physical Sciences and Engineering
Chemistry
Physical and Theoretical Chemistry
Authors
Moon Hyung Jang, Kwang Sik Jeong, Kwun Bum Chung, Jin Woo Lee, Myeung Hee Lee, Mann-Ho Cho,