Article ID Journal Published Year Pages File Type
5436088 Acta Materialia 2017 15 Pages PDF
Abstract

We investigate the mechanical behavior of 3D periodically architected metallic glass nanolattices, constructed from hollow beams of sputtered Zr-Ni-Al metallic glass. Nanolattices composed of beams with different wall thicknesses are fabricated by varying the sputter deposition time, resulting in nanolattices with median wall thicknesses of ∼88 nm, ∼57 nm, ∼38 nm, ∼30 nm, ∼20 nm, and ∼10 nm. Uniaxial compression experiments conducted inside a scanning electron microscope reveal a transition from brittle, catastrophic failure in thicker-walled nanolattices (median wall thicknesses of ∼88 and ∼57 nm) to deformable, gradual, layer-by-layer collapse in thinner-walled nanolattices (median wall thicknesses of ∼38 nm and less). As the nanolattice wall thickness is varied, large differences in deformability are manifested through the severity of strain bursts, nanolattice recovery after compression, and in-situ images obtained during compression experiments. We explain the brittle-to-deformable transition that occurs as the nanolattice wall thickness decreases in terms of the “smaller is more deformable” material size effect that arises in nano-sized metallic glasses. This work demonstrates that the nano-induced failure-suppression size effect that emerges in small-scale metallic glasses can be proliferated to larger-scale materials by the virtue of architecting.

Graphical abstractDownload high-res image (350KB)Download full-size image

Related Topics
Physical Sciences and Engineering Materials Science Ceramics and Composites
Authors
, ,