Abstract
Solid state sintering, liquid phase and cooling stages play different roles in determining the final morphology and composition of cermets, especially the well-known core-rim structure. In this work, TiC-(5-25 wt%)WC-11Mo2C-18(Ni-Co) cermets were prepared and sintered by different sintering schedules. Morphology evolution and rim phase composition during sintering from 1250 °C to 1600 °C were investigated. Effects of sintering stages on the final morphology of cermets were also studied. It was shown that submicron (Ti, W, Mo)C grains tend to precipitate in binder during the cooling for cermets with high WC content. After the formation of outer rims during liquid sintering stage, interface reaction began to take effect between the rims and core. Coreless (Ti0.76, W0.13, Mo0.11)C ceramic grains would be formed under high temperature (1600 °C) for TiC cermets with 25% WC. Long time sintering at solid state favored the formation of black core-thick inner rim and bright core-grey rim phases, while cooling near the melting point could result in submicron bright particles. This study provided not only a better view of the formation of rim-core structure but also an easier way to control the final morphology of cermets via reasonable changing the sintering cycle.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Huiwen Xiong, Zhi you Li, Xueping Gan, Liyuan Chai,