Abstract
This paper reports the preparation of Eu3+ doped Gadolinium oxyorthosilicate (Gd2SiO5:Eu3+) phosphor with different concentration of Eu3+(0.1-2.5Â mol%) using the modified solid state reaction method. The synthesis procedure of the Gd2SiO5:Eu3+phosphor using inorganic materials such as Gd2O3, silicon dioxide (SiO2), europium oxide (Eu2O3) and boric acid (H3BO3) as flux is discussed in detail. The prepared phosphor samples were characterized by using X-Ray Diffraction (XRD), Field Emission Gun Scanning Electron Microscopy (FEGSEM), Transmission Electron Microscopy (TEM), Fourier Transform Infrared Spectroscopy (FTIR), Photoluminescence (PL) and Thermoluminescence (TL). The Commission Internationale de lâ²Eclairage(CIE) coordinates were also calculated. The PL emission was observed in the 350-630Â nm range for the Gd2SiO5:Eu3+ phosphor. PL excitation peaks were observed at 266, 275, 312 and 395Â nm while the emission peaks were observed at 380, 416, 437, 545, 579, 589, 607, 615 and 628Â nm. The emission peak at 615Â nm was the most intense peak for all the different Eu3+ concentration samples. From the XRD data, using the Scherrer's formula, the average crystallite size of the Gd2SiO5:Eu3+ phosphor was calculated to be 33Â nm. TL was carried out for the phosphor after both UV and gamma irradiation. The TL response of the Gd2SiO5:Eu3+ phosphor for the two different radiations was compared and studied in detail. It was found that the present phosphor can acts as a single host for red emission (1.5Â mol%) for display devices and light emitting diode (LED) and white light emission for Eu3+(0.1Â mol%) and it might be used as a TL dosimetric material for gamma dose detection.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Yogita Parganiha, Jagjeet Kaur, Neha Dubey, Vikas Dubey, Ravi Shrivastava, S.J. Dhoble, Hendrik C. Swart,