Porous SiC/SiCN composite ceramics fabricated by foaming and reaction sintering

Porous SiC/SiCN composite ceramics with heterogeneous pore structure and rod-like SiCN grains were fabricated by foaming and reaction sintering. The mixture slurry containing SiC and silicon as raw materials, cornstarch as binder, Y2O3 as sintering additive and an electrosteric dispersant was stirred with foams derived from pre-foaming using foaming agent. The casted green body was sintered at 1650 °C under nitrogen atmosphere. The results demonstrated that the porous SiC/SiCN ceramics exhibited hierarchical vias ranging from 1 μm to 1 mm and the rod-like crystalline SiCN grains generated in the SiC matrix.