The microstructure, coefficient of thermal expansion and flexural strength of cordierite ceramics prepared from alumina with different particle sizes

Cordierite ceramics were produced from alumina with 5 and 0.65 μm particle sizes or AlOOH and talc, clays and feldspar, to determine the influence of the alumina particle size on the microstructure, coefficient of thermal expansion (CTE) and flexural strength (FS) of the ceramics. After sintering at 1300 °C the ceramics made from 5-μm-sized alumina consisted of cordierite, glass, quartz, mullite and alumina, and had the highest density, FS and CTE. The alumina grains act as inclusions, from which the trajectories of the cracks were deflected or terminated, which increases the FS and CTE. The ceramics from sub-micrometre-sized alumina or AlOOH contained a negligable amount and no alumina, respectively, together with other phases. This is reflected in the low CTE and FS. The cordierite ceramic with the lowest CTE of ∼2.0 × 10−6 K−1 and a high FS of 100 MPa was prepared from the 0.65-μm-sized alumina particles.