Enhanced electrochemical performance from 3DG/LiFePO4/G sandwich cathode material

In this paper, we have successfully synthesized a three dimensional graphene/LiFePO4/graphene (3DG/LFP/G) sandwich composite by an in-situ hydrothermal method, in which chemical vapor deposited 3D graphene acts as the high conductivity supporting framework, while the LiFePO4 nanoparticles are anchored onto the 3D graphene framework covered by graphene sheets. XRD and SEM results confirmed the formation of the 3DG/LFP/G sandwich composite. Cyclic Voltammetry curve of the sandwich composite shows sharper redox peaks and reduced voltage separation when compared to the reference electrodes, suggesting high specific capacity and good rate performance. Further charge/discharge measurements presented high capacity of 164 mAh g−1 at 0.2 C and 124 mAh g−1 at 10 C (75.7% of its initial capacity) for the sandwich composite, with capacity retention of 95.7% after 100 cycles, implying potential application in lithium ion battery at high rates. The EIS investigation suggests that both the electronic conductivity and the Li ion diffusion are promoted by the underlined 3D graphene framework, which is regarded as the reason for the enhanced electrochemical performance.