Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
5455392 | Materials Science and Engineering: A | 2017 | 9 Pages |
Abstract
The microstructure and tensile properties of as-extruded AZ91 alloy with 1.0Â wt% Ca, 0.5Â wt% Si, 0.1Â wt% La and 0.1Â wt% Ce additions (was named AZXSE91100 alloy) were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The addition of multiple elements results in various compounds forming in as-cast alloys. On one hand, the massive large particles are good for grain refinement of as-extruded alloy, which can promote dynamic recrystallization (DRX) during extrusion process via the mechanism of particle stimulated nucleation (PSN). On the other hand, through hot extrusion, the coarse second phases are fragmented into finer dispersed particles including lots of heat-resistant compounds, such as CaMgSi, Mg2Si, Al2RE, which play an important role in hindering dislocation motions and grain boundary sliding at elevated temperature. Accordingly, the best tensile properties at room temperature are obtained from the peak-aged as-extruded AZXSE91100 alloy, and yield stress (YS), ultimate tensile stress (UTS) and elongation (EL) are 310Â MPa, 370Â MPa and 8.9%, respectively. The best tensile properties at elevated temperature are obtained from as-extruded AZXSE91100 alloy, and YS, UTS and EL at 423Â K reach 222Â MPa, 230Â MPa and 25.9%, respectively.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
Chaojie Che, Zhongyi Cai, Xiaohong Yang, Liren Cheng, Yunqiu Du,