Abstract
A diffusion-modified HfC/HfCSiC bilayer system was innovatively designed and synthesized onto cemented carbide (WC-Co) substrate by reactive double glow plasma surface alloying (DGPSA) technique for adherent diamond deposition. The microstructure, phase composition and adhesion of the bilayer system were investigated, as well as its effect on the diamond coating system. The results showed that the bilayer system was made up of a 1.0-μm-thick nanostructured HfC-dominant inner layer and a 0.7-μm-thick HfCSiC mixed outer layer. As the gradient element distributions existed at the bilayer/substrate interface, the bilayer system displayed a superior adherence to the substrate. And the surface microhardness improved from 1802 HV0.1 to 2857 HV0.1 after the reactive DGPSA treatment. Subsequently, a uniform and dense nanocrystalline diamond coating with thickness of 4.0 μm was successfully deposited onto the HfC/HfCSiC interlayered substrate. Benefit from the effective suppression of Co diffusion by the interlayer and the reasonable design in its hardness and thermal expansion coefficient (TEC), the obtained diamond coating possessed an excellent adhesion. Therefore, the diffusion-modified HfC/HfCSiC bilayer systems synthesized via reactive DGPSA technique can be considered as a novel interlayer option for depositing adherent diamond coatings on WC-Co substrates.
Keywords
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
Jie Gao, Hongjun Hei, Ke Zheng, Rong Wang, Yanyan Shen, Xiaoping Liu, Bin Tang, Zhiyong He, Shengwang Yu,