Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
5464720 | Surface and Coatings Technology | 2017 | 39 Pages |
Abstract
To improve the oxidation resistance under thermal shock condition of SiC-coated carbon/carbon (C/C) composites, ferrocene ((C5H5)2Fe) was introduced in the SiC coatings during the pack cementation process. The microstructure and oxidation resistance under thermal shock condition of modified SiC coated C/C composites were studied. The HNO3 treatment and the introduction of (C5H5)2Fe could raise the nucleation point and the decomposition of (C5H5)2Fe can slow down the sintering process, which helps to decreased the sizes of SiC particles and micro-defects (including micro-cracks and micro-holes) and resulted in a relatively dense structure. Thermal shock test revealed that the mass change rate of C/C composites decreased from 18.25% to 10.08% after thermal cycle test between 1773Â K and room temperature for 25 times, suggesting a better shock resistance for the modified SiC coating compared with the base coatings (without modification). This work provides a novel way to modify the SiC coating capable of releasing the thermal residual stress and decreasing the oxygen diffusion channels and then further increasing the oxidation resistance under thermal shock condition of C/C composites without other supplementary protective coatings.
Related Topics
Physical Sciences and Engineering
Materials Science
Nanotechnology
Authors
Caixia Huo, Lingjun Guo, Lei Feng, Changcong Wang, Zhaoqian Li, Yulei Zhang, Gang Kou,