In situ micro-compression testing of He2+ ion irradiated titanium aluminide

A titanium aluminide (TiAl) alloy 45XD has been irradiated by a He ion beam with an energy of 5 MeV on a tandem accelerator at the Australian Nuclear Science and Technology Organization (ANSTO). The total fluence of He ions was 5 × 1017 ion cm−2. A 17 μm uniform damage region from the material surface with a helium concentration of about 5000 appm was achieved by using an energy degrading wheel in front of the TiAl target. The micro-size test specimens from the damage layer were fabricated using a focused ion beam & scanning electron microscope (FIB-SEM) system. The in situ SEM micromechanical compressive testing was carried out inside an SEM and the results indicated irradiation embrittlement in the helium affected region. Electron back scatter diffraction (EBSD) analysis has been applied to reveal the orientation of the lamellae in the TiAl specimens, and used to understand the deformation processes in the sample. The irradiation damage of gallium ion beam from FIB on the surface of TiAl sample was also investigated.