Abstract
The Co-96.9 wt% Sb hypoeutectic alloy doped by 0.12 wt% YbFe was solidified in a Bridgman-type furnace based on temperature gradient zone melting (TGZM) effect. A mushy zone was observed between the complete liquid zone and the solid zone at different thermal stabilization time ranging from 15 min to 40 h. The mushy-zone solidified microstructures of the alloy only consist of CoSb3 and Sb phase. After 40 h thermal stabilization time, the volume fraction of CoSb3 in the mushy zone increases significantly up to 99.6% close to the solid-liquid interface. The hardness and fracture toughness of doped CoSb3 can reach 7.01 ± 0.69 GPa and 0.78 ± 0.08 MPa·m1/2, respectively. Meanwhile, the thermoelectric properties of the alloy were measured ranging from room temperature (RT) to 850 K. The Seebeck coefficient of the specimen prepared by TGZM effect after 40 h could reach 155 μV/K and the ZT value is 0.47 at 660 K, showing that it is feasible to prepare CoSb3 bulk material via TGZM effect. As a simple and one-step solidification method, the TGZM technique could be applied in the preparation of skutterudite compounds.
Related Topics
Physical Sciences and Engineering
Physics and Astronomy
Condensed Matter Physics
Authors
Hongqiang Wang, Shuangming Li, Xin Li, Hong Zhong,