Effect of Gd3+ substitution on structural, magnetic, dielectric and optical properties of nanocrystalline CoFe2O4

Nanoparticles of CoGdxFe2−xO4 with x=0.0, 0.03, 0.05, 0.07, 0.10 and 0.15 were synthesized by co-precipitation method. Gd3+ substitution effect on different properties of nanocrystalline CoFe2O4 has been studied. X-ray diffraction and Raman spectroscopy confirmed the formation of single phase cubic mixed spinel structure. Cation distribution has been proposed from Rietveld refined data. Mössbauer spectra at room temperature showed two ferrimagnetic Zeeman sextets with one superparamagnetic doublet. Mössbauer parameters suggested that Gd3+ ions occupy the octahedral site in CoFe2O4. Room temperature magnetic measurements exhibited that the saturation magnetization decreased from 91 emu/gm to 54 emu/gm for x=0.0 to 0.15 samples. The coercivity decreased from 1120 Oe to 340 Oe for x=0.0 to 0.07 samples and increased from 400 Oe to 590 Oe for x=0.10 and 0.15 samples, respectively. Raman analysis showed that the degree of inversion with Gd3+ substitution supporting the variation of coercivity. Electron spin resonance spectra revealed the dominancy of superexchange interactions in these samples. Optical band gap measurement suggested that all samples are indirect band gap materials and band gap has been decreased with Gd3+ substitution. Both dielectric constant and dielectric loss is found to decrease because of the decrease in hopping rate with the Gd3+ substitution for Fe3+ at the octahedral sites. Low dielectric loss suggested the applicability of Gd3+ doped CoFe2O4 nanoparticles for high frequency microwave device applications.