Abstract
According to the formula Sr0.95Y0.05Fe12âxCoxO19 (x = 0.00, 0.08, 0.16, 0.24, 0.32, 0.40), the replacement of Y-Co in M-type strontium hexagonal ferrites have been successfully prepared by ceramic process for the first time. The phase compositions of magnetic powders were examined by X-ray diffraction. The results of XRD showed that the single phase was obtained in magnetic powders with the increase of Co content (x), and α-Fe2O3 occurred when x > 0.24. The morphology of the magnets was investigated by scanning electron microscopy (SEM). The micro-morphology of the particles exhibited the uniform plane hexagonal structures of M-type ferrites with different Co content. Magnetic properties of the ferrite magnets were measured by a physical property measurement system-vibrating sample magnetometer (PPMS-VSM). The Ms increases constantly with the increase of Co content. The Hc first increases and then decreases with the increase of Co content, and the value of coercivity (Hc) is up to 3774 Oe when x = 0.24.
Keywords
Related Topics
Physical Sciences and Engineering
Physics and Astronomy
Condensed Matter Physics
Authors
Chaocheng Liu, Xiansong Liu, Shuangjiu Feng, Khalid Mehmood Ur Rehman, Mingling Li, Cong Zhang, Haohao Li, Xiangyu Meng,