Obtaining Crack-free WC-Co Alloys by Selective Laser Melting

Standard hardmetals of WC-Co system are brittle and often crack at selective laser melting (SLM). The objective of this study is to estimate the range of WC/Co ratio where cracking can be avoided. Micron-sized Co powder was mixed with WC nanopowder in a ball mill to obtain uniform distribution of WC over the surface of Co particles. Continuous layers of remelted material on the surface of a hardmetal plate were obtained from this composite powder by SLM at 1.07μm wavelength. The layers have satisfactory porosity and are well bound to the substrate. The chemical composition of the layers matches the composition of the initial powder mixtures. The powder mixture with 25wt.%WC can be used for SLM to obtain materials without cracks. The powder mixture with 50wt.%WC cracks because of formation of brittle W3Co3C phase. Cracking can considerably reduce the mechanical strength, so that the use of this composition is not advised.