The thermal decomposition reaction of crystalline heteronuclear cyano complex precursor to crystalline perovskite-type oxide catalyst was investigated. From X-ray single crystal analysis and XRD, FT-IR, TG-DTA, SEM, and BET measurements, the thermal decomposition process of Sm[Fe(CN)6]·4H2O precursor was elucidated. It was found that the specific surface area of SmFeO3 decreased monotonously with increasing calcination temperature of Sm[Fe(CN)6]·4H2O, while the highest catalytic activity for CO oxidation was achieved for Sm[Fe(CN)6]·4H2O calcined at 600 °C. The size of Sm[Fe(CN)6]·4H2O precursor depended on the molar concentration of starting materials, Sm(NO3)3·6H2O and K3Fe(CN)6, in aqueous solution (Cs); the size of Sm[Fe(CN)6]·4H2O decreased with decreasing Cs. The decrease in particle size of cyano complex was found to result in the increase in specific surface area of perovksite-type oxide obtained after calcination.

Graphical abstractFigure optionsDownload full-size imageDownload high-quality image (337 K)Download as PowerPoint slideHighlights► Cyano complex was transformed into perovskite-type oxide by thermal treatment at ca. 600 °C. ► The shape and the size of cyano complex particle were dependent on the concentration of aqueous solution of starting materials. ► The small particle of cyano complex provided that of perovskite-type oxide by thermal treatment, exhibiting a high surface area and a high catalytic activity.

Related Topics
Physical Sciences and Engineering Chemical Engineering Catalysis
Authors
, , , ,