A titanium nitride (TiN) coating was deposited by magnetron sputter ion plating onto steel and titanium alloy polished substrates. The adhesion of the coating on each substrate material was investigated using a newly developed multimode scratch tester. Progressive loading scratch tests, constant load scratch tests, multiple scratch tests in the same track and indentation tests were all performed. It was shown that the modified scratch tester can be used to identify not only coating detachment during progressive load scratch tests, but also other failure events such as cracking and cohesive damage to the coatings. By using the additional modes of operation, it was possible to study the fracture mechanisms in more detail i.e. chipping in the scratch track was cohesive for the TiN coated steel and adhesive for the TiN coated Ti alloy.