A study on erosion of upper bainitic ADI and PDI

For 2.1Si-ADI and 2.8Si-ADI tempered for a short duration, increasing the volume fraction of martensite in the matrix increases the erosion rate at an impact angle of 30°, but the maximum erosion rate is found at 75°. This results in a curve with a double peak. The double peak curve was also observed for high silicon ADI tempered for a long duration. The high solid solution hardness of 4.2Si-ADI, due to low retained austenite content and the presence of carbide in the matrix, results in poor erosion resistance. When this material is austempered for a long period, the erosion rate curve shifts from a single peak curve (30°) to a double peak curve (30°; 60°).