Recently nanofiltration (NF) is gaining more importance for water treatment. It is replacing the conventional method of water treatment due to advantages of NF membranes over RO system. In this work, we are discussing the preparation of NF membrane for desalination of sea water. We herein report the synthesis of polymer, by the reaction of p-amino benzoic acid (PABA) and poly isobutylene-alt-maleic anhydride (PIAM) and its blend membrane preparation with polysulfone (PSf). The new membranes were characterized by SEM images, surface wettability to investigate the hydrophilic nature of the membrane, water swelling, pure water flux, molecular weight cut-off and salt rejection of the membranes. The membranes showed nano size (< 50 nm) pores in SEM image, and the contact angle data revealed that membrane surface is moderately hydrophilic. Membrane with 70:30 (PSf:modified PIAM) composition has shown good salt rejection of 96% at 200 kPa for 3500 ppm of NaCl solution with a pure water flux of 38.36 Lm− 2 h− 1.
Graphical abstractModification of poly isobutylene-alt-maleic anhydride (PIAM) and its blend membrane preparation with polysulfone (PSf). NF membrane with 70:30 (PSf:modified PIAM) composition has shown good salt rejection of 96% at 200 kPa for 3500 ppm NaCl solution with a water flux of 38.36 Lm−2 h−1.Figure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Poly isobutylene Co maleic anhydride was modified. ► NF membrane was prepared from modified PIAM and PSf. ► Membranes were characterized. ► NF membrane with 70:30 composition has shown salt rejection of 96%.