Abstract
The average size of the alumina grains was 1 μm, and neither whiskers nor extremely flat grains were observed. About one-third of the grains had smooth surfaces, while â¼60% of the grains had rough surfaces with 10-100 nm-sized fine structures. The rough-surface grains have varieties of morphology and crystallinity, suggesting that the rough surface structures are secondary in origin. Electron back-scattered diffraction patterns from 95% of alumina grains matched with α-Al2O3 (corundum), and more than 75% of the alumina grains are single crystals of corundum. Nine presolar alumina grains with anomalous oxygen isotopic compositions were found among 107 alumina grains, and most of them were characterized by rough surface structures. While most of the presolar alumina grains were corundum, the relative abundance of amorphous or low-crystallinity grains is higher in presolar alumina grains than in solar alumina grains. The dissolution experiments showed that all phases except for corundum dissolved during the acid treatments of chondrites. This suggests that smooth surface structures of corundum grains were originally formed in space, and that original surfaces of alumina that had been damaged by energetic particle irradiation in the ISM or the protosolar disk were lost during chemical separations to form the rough surface structures, and that amorphous or low-crystallinity alumina grains in chondrites have acid-resistant structures different from sol-gel-synthesized amorphous alumina. The present results also imply the possible presence of acid-soluble alumina phases, undiscovered by chemical separations, in chondrites.
Related Topics
Physical Sciences and Engineering
Earth and Planetary Sciences
Geochemistry and Petrology
Authors
Aki Takigawa, Shogo Tachibana, Gary R. Huss, Kazuhide Nagashima, Kentaro Makide, Alexander N. Krot, Hiroko Nagahara,