â¢The CO2 methanation performance of cobalt-based catalysts is explored.â¢The impact of support (CeO2, ZrO2, Gd2O3, ZnO) was investigated.â¢Co/CeO2 catalyst exhibited an up to 100% conversion of CO2 to methane at 300 °C.â¢The superiority of Co/CeO2 catalyst can be ascribed to its enhanced reducibility.â¢Co/ZnO catalyst was progressively activated under reaction conditions.
CO2 hydrogenation to value added chemicals/fuels has gained considerable interest, in terms of sustainable energy and environmental mitigation. In this regard, the present work aims to investigate the CO2 methanation performance of cobalt-based catalysts supported on different metal oxides (MxOy: CeO2, ZrO2, Gd2O3, ZnO) at low temperatures (200-300 °C) and under atmospheric pressure. Various characterization methods, such as N2 adsorption-desorption at â196 °C, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction (TPR), were employed to correlate the structural and surface properties of the materials with their catalytic activity. The results revealed a significant impact of support nature on the CO2 hydrogenation performance. The following order, in terms of CH4 yield (YCH4), was recorded at 300 °C: Co/CeO2 (â¼96%) > Co/ZnO (â¼54%) > Co/G2O3 (â¼53%) â¼Â Co/ZrO2 (â¼53%). On the basis of the characterization results, the superiority of Co/CeO2 catalyst can be mainly ascribed to its enhanced reducibility linked to Co-Ceria interactions. Moreover, Co/CeO2 demonstrated a stable conversion/selectivity performance under subsequent reaction cycles, in contrast to Co/ZnO, which progressively activated under reaction conditions. The latter is related with the modifications induced in elemental chemical states and surface composition of Co/ZnO upon pretreatment in reaction conditions, in contrast to Co/CeO2 sample where a stable surface performance was observed.
Graphical abstractDownload high-res image (169KB)Download full-size image