Preparation and electrochemical performances of NiS with PEDOT:PSS chrysanthemum petal like nanostructure for high performance supercapacitors

•NiS/PEDOT:PSS with DEG chrysanthemum petals were prepared using a facile bar-coating method.•NiS/PEDOT:PSS with DEG showed greater electrochemical properties.•Improved penetration of electrolyte ions into the electrode was observed by the attachment PEDOT:PSS on NiS.•The electrode exhibited a high specific capacitance of 750.64 F g−1 at 1.11 A g−1.•The nanocomposite displayed excellent cycling stability.

This paper reports the facile synthesis of a novel architectural of NiS/PEDOT:PSS with DEG, where the complementary features of the three components (well-defined NiS black pepper like nanoparticles on nickel foam, an ultrathin layers of poly (3,4-ethylenedioxythiophene)/poly(styrenesulfonate) (PEDOT:PSS), and diethylene glycol (DEG)) are deposited sequentially to a single entity to fabricate a high-performance electrode for supercapacitor applications. Owing to the high electrical conductivity of the well-defined NiS nanoparticles, in which the conductivity, and good chemical and electrochemical stability is enhanced further by the PEDOT:PSS and DEG thin layers, the as-fabricated NiS/PEDOT:PSS with a DEG chrysanthemum petal-like nanostructure exhibits good rate capability, excellent cycling stability, and high specific capacitance. The PEDOT:PSS with DEG offers extra conductive paths for each layer on NiS, yielding a lower internal resistance and charge-transfer resistance than that of the NiS/PEDOT:PSS without DEG. As a result, the NiS/PEDOT:PSS with the DEG electrode shows a tremendous pseudocapacitance of 750.64 F g−1 at 1.11 A g−1, along with a high energy density of 24.52 Wh kg−1 at a power density of 138.88 W kg−1 and good cycling stability, suggesting that it is a promising candidate for energy storage. The unique performance of NiS/PEDOT:PSS with a DEG benefits from its unique chrysanthemum petal-like nanostructure, which could offer faster ion and electron transfer ability, greater reaction surface area and good structural stability.

Graphical abstractDownload high-res image (167KB)Download full-size image