Unusual temperature effect on the stability of nickel anodes in molten carbonates

•The anodic behaviour of nickel in molten carbonates was investigated.•An unusual temperature effect on the stability of nickel anode was revealed.•An activation-passivation transition temperature was found to exist at 575 °C.•A mechanism was proposed to describe the nickel anode temperature effect.

The stability of nickel anode in a eutectic molten Li2CO3-Na2CO3-K2CO3 electrolysis cell was systematically investigated over the temperature range of 450 °C to 750 °C. An unusual temperature effect was observed involving a critical activation-passivation transition temperature at 575 °C for the nickel in the melt; rapid dissolution of nickel was found to occur below 575 °C under anodic polarization, whereas its surface became passivated above this temperature, and the stability of the passivation film was further improved by increasing the temperature up to 750 °C. A blackish oxide film forms on nickel surfaces that retard the anodic dissolution of nickel. The composition and structure of the oxide film, as well as its formation mechanism, were studied by electrochemical measurements combined with X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) characterization. Two temperature sensitive oxidation states of nickel (i.e., Ni(II) and Ni(III)) formed during the anodic polarization. Ni(III) tended to combine with Li2CO3 to form the more soluble LiNiO2 during anodic polarization at lower temperature, and its content in the film decreased dramatically with increasing temperature. Thus, a stable and protective film consisting of NiO can form at temperatures above 575 °C.

Graphical abstractThe electrochemical stability of nickel increases with temperature during anodic polarization in molten Li2CO3-Na2CO3-K2CO3, with a critical activation-passivation transition temperature at 575 °C.Download high-res image (194KB)Download full-size image