Time dependence of characteristic parameter for semi-volatile organic compounds (SVOCs) emitted from indoor materials

•Significant decrease of y0 of TCPP in polyurethane foam over three months.•Much lower decrease of y0 of DEHP in PVC materials.•y0 decrease rate is positively related to SVOC vapor pressure.•Discussions about potential reasons for y0 decrease are presented.

Semi-volatile organic compounds (SVOCs) are widely used in various indoor materials and their adverse health effects have been increasingly recognized. The gas-phase SVOC concentration in equilibrium with the source material (y0), as a characteristic parameter for SVOC sources, is mostly assumed to be constant in previous studies. However, decreases in y0 with time have been observed in some studies. As a first step to reveal the mechanism behind the phenomenon, this study quantitatively investigated the variation of y0 over time under two conditions: natural exposure to outdoor ambient (Case 1), and storage in a controlled ventilated chamber (Case 2). Three phthalates (Di-iso-butyl Phthalate (DiBP), Di-n-butyl Phthalate (DnBP), and di-(2-ethylhexyl) phthalate (DEHP)) emitted from polyvinyl chloride (PVC) floorings and one flame retardant (tris(2-chloroisopropyl) phosphate, TCPP) emitted from polyurethane foam (PUF) were targeted. Experimental results indicated that, for SVOCs with higher volatility, i.e., DiBP, DnBP, and TCPP, y0 decreased 16%-49% after 60 days' exposure for Case 1; and 16%-36% for Case 2. For SVOCs with lower volatility, i.e., DEHP, no significant decrease in y0 was observed after 60 days in both cases; while if prolonging the time to about 1.5 years, a decrease of 38% was observed. Discussion about potential reasons for the decrease of y0 was presented. The results obtained here provide a further understanding about SVOC source characteristics and therefore help providing source strength for estimating indoor SVOC health exposure.