Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
6607346 | Electrochimica Acta | 2016 | 28 Pages |
Abstract
The high voltage LiNi0.5Mn1.5O4 cathode with a disordered spinel structure is synthesized by a glycine-assisted low-temperature reaction follows by a thermal treatment at 750 °C, 850 °C, and 950 °C for 12 h. Glycine is used as a chelating agent for the first time to build required environment for shaping the precursor of LiNi0.5Mn1.5O4 materials. The microstructure and morphology of the LiNi0.5Mn1.5O4 product are characterized by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, Brunauer-Emmett-Teller, and transmission electron microscopy. The sample prepares at 750 °C reveals small particles with well-defined crystals as confirmed by electron microscopy. Electrochemical results demonstrate that LiNi0.5Mn1.5O4 electrode anneal at 750 °C (compare to other two samples) delivers the highest reversible capacity of 110 mAh gâ1 at 0.2C after 100 cycles with good rate capability. The enhanced electrochemical performance could be attributed to the smaller particle sizes as well as well-defined crystals which provide a directional and shorter diffusion path length for Li+ transportation within the crystals.
Related Topics
Physical Sciences and Engineering
Chemical Engineering
Chemical Engineering (General)
Authors
Nur Diyana Rosedhi, Nurul Hayati Idris, Md Mokhlesur Rahman, M.F. Md Din, Jianli Wang,