The effect of some wood preservatives on the thermal degradation of Scots pine

Wood has been a structural material for many years; however, its ability to burn has limited its use in some applications. This study aims to evaluate the effect of commercial wood preservatives having concentration of 4% on the thermal behavior of Scots pine wood, and compare the fire retardant effectiveness of these preservatives with that of boron compounds. Thermal degradation of treated and untreated wood samples was evaluated by thermogravimetry (TG), differential thermogravimetry (DTG) and differential thermal analysis (DTA). Thermal behavior of treated wood differed from thermal behavior of untreated wood in terms of a high char yield. Results showed that weight loss of wood reduced while char yield increased in the charring phase of the pyrolysis in the boron containing preservative treated wood accompanying with pyrolysis temperature lowered. The highest char yield was obtained from the samples treated with disodium octaborate tetrahydrate in the all treated groups.

► Scots pine samples were impregnated with 10 commercial wood preservatives. ► Thermal degradation of wood was evaluated by TG, DTG and DTA. ► The thermal behavior of treated wood differed from that of untreated wood. ► Boron containing wood preservatives yielded more charcoal than other preservatives. ► Boric oxide and metal compounds in the formulations may affect char weight.